Powlex Resinβ-HAA (PRIMID), Services

Powlex Resinβ-HAA (PRIMID) Product details.
Images

β-HAA (PRIMID)

Outdoor Applications Waiting for product details...
View Catalog
About

Resin for β-HAA (PRIMID) Systems

PRODUCT Name Ratio Gas Oven Stable Overbake Stable Tribo AV Viscosity (cP) Tg (0C) Cure T (0C)/t (min) Explanation
P183-2 97/3 * * 20-25 5400-8200 approx.62 180/10 For matte powder coatings by dry blending with P187 and P181
P183-3 97/3 * * * 20-25 5400-8200 approx.62 180/10 Tribo version of P183-2. For matte powder coatings by dry blending with P187 and P181
P184-2 96,5/3,5 * * 21-25 5600-8100 approx.61 180/10 For low level Primid, excellent flow, overbake and gas oven resistance.
P184-3 96,5/3,5 * * * 21-25 5600-8100 approx.61 180/10 Tribochargeable version of P184-2
P185-2 95/5 * * 30-36 2500-3500 approx.60 180/10 Excellent weathering and very good flow. Overbake and gas oven resistance.
P185-3 95/5 * * * 30-36 2500-3500 approx.60 180/10 Tribochargeable version of P185-2
P187-0 93/7 49-54 3000-5500 approx.58 180/10 For matte powder coatings by dry blending with P183
P187-3 93/7 * * * 49-54 3000-5500 approx.58 180/10 Tribo activated version of P187-0. For matte powder coatings by dry blending with P183
P181-0 90/10 75-85 1000-3000 approx.58 180/10 For matte powder coatings by dry blending with P183
P181-3 90/10 * * * 75-85 1000-3000 approx.58 180/10 Tribo version of P181-0 For matte powder coatings by dry blending with P183
AP185-3 95/5 * * * 33-37 2300-3600 approx.54 180/10 Enhanced architectural β-HAA resin , excellent flow and degassing properties up to 160 microns. Overbake and gas oven resistance.
P165-3 95/5 * * * 34-38 2500-4500 approx.56 160/10 Low temperature curable β-HAA resin for industrial application. It is non-blooming
P157-3 93/7 * * * 45-51 4300-7300 approx.58 150/10 Low bake resin when 7% HAA is used
SP183-0 97/3 18-22 3500-5500 approx.60 200/10 Dry blended with SP188-0 to obtain 30 gloss surface
SP185-0 95/5 30-36 3000-4400 approx.59 190/10 Superdurable resin with good mechanical properties. It can be formulated with both β-HAA and TGIC. It has blooming resistance
SP185-3 95/5 * * * 30-36 3000-4400 approx.59 190/10 Tribo version of SP185-0
SP188-0 92/8 49-54 4500-6600 approx.64 200/10 Dry blended with SP183-0 to obtain 300 gloss surface
DM204-0 23-27 5000-6400 approx.58 200/10 Slow reactive component for dull Matte One Shot (5-10 gloss)
DM201-0 88-92 2700-4600 approx.62 200/10 Fast reactive component for dull Matte One Shot (5-10 gloss)

GLOSSARY
Acid Value (mg KOH/gr) The amount of KOH necessary to neutralize the acid content in one gram of polyester.
Blooming A hazy appearance on the surface of the coating by migration of low molecular weight material during low temperature cure or extended exposure to heat.
Epoxy Equivalent Weigth (EEW) The weight of resin containing one gram-equivalent of epoxy.
Glass Transition Temperature (Tg) The characteristic temperature in °C of an amorphous polymer corresponding to the change from a solid to liquid state as measured by DSC.
Hydroxy Value (OH V) The amount of KOH equivalent to the hydroxyl content of one gram of polyester.
Low Bake A property of baking using temperatures in below 1600C
Matte A coating appearance that reflects a minimal amount of light.
Ratio Weight ratio between the polyester resin and the hardener.
Storage Stability Ability of powder coatings to maintain free flow powder properties after being subjected to a specified storage condition.
Superdurable A polyester resin that exhibits extended outdoor weathering characteristics, typically maintaining > 50 % gloss retention after 3 years (EU) and min. 30% gloss retention after 5 years (US) exposed in Florida
Wrinkle A unique, special effect characterized with ridge-like structures.